This C14 LT Lithium Disilicate Glass Ceramic Block is designed for dental CAD/CAM milling systems. Size: C14 (18mm × 13mm × 15mm). Color Set: A1, A2, A3, A3.5, A4. Transparency: LT (low transparency).
Explore More637MPa USP : Justifies premium over 400MPa competitors. Li₂O 11-17% Lithium Disilicate Crystals. LT (Low Trans) A1-A3.5 • B1-B2 • BL1-BL4 • C1-C2 🔹Molars 🔹Discolored Teeth. PRO TIP : Pair with “YUSENDENT Crystallization Furnace” for perfect results!
Explore MoreDental glass ceramics, Main ingredients are Lithium Disilicate, through special process. Bending strength The average biaxial bending strength after being fully crystallized is 637Mpa, higher than the standard strength value, set by ISO6892:2008 For Dental Ceramics.
Explore MoreEasy Processing: Low hardness before crystallization, allowing for smooth, precise milling with CAD/CAM systems (compatible with CEREC, inLab, PlanMill, and more) and extending bur life. Our C14 Dental Glass Ceramic is a premium lithium disilicate-based material, engineered with a unique glassy zirconia matrix and dual crystal structure to achieve the perfect balance of strength, aesthetics, and processing efficiency.
Explore MoreDental glass ceramics, Main ingredients are Lithium Disilicate, through special process. HT–High Transparency. HT– A1, A2, A3,B1,B2, BL1, BL2, BL3, BL4. Bending strength The average biaxial bending strength after being fully crystallized is 637Mpa, higher than the standard strength value, set by ISO6892:2008 For Dental Ceramics.
Explore MoreDental glass ceramics, Main ingredients are Lithium Disilicate, through special process. Bending strength The average biaxial bending strength after being fully crystallized is 637Mpa, higher than the standard strength value, set by ISO6892:2008 For Dental Ceramics.
Explore MoreLT— A1, A2, A3,A3.5. Dental glass ceramics, Main ingredients are Lithium Disilicate, through special process. Bending strength The average biaxial bending strength after being fully crystallized is 637Mpa, higher than the standard strength value, set by ISO6892:2008 For Dental Ceramics.
Explore MoreDental glass ceramics, Main ingredients are Lithium Disilicate, through special process. Bending strength The average biaxial bending strength after being fully crystallized is 637Mpa, higher than the standard strength value, set by ISO6892:2008 For Dental Ceramics.
Explore MoreSize: C14 (18x13x15mm). Bending strength The average biaxial bending strength after being fully crystallized is 637Mpa, higher than the standard strength value, set by ISO6892:2008 For Dental Ceramics.